Published in: Odontology 2/2019

01-04-2019 | Original Article

Effects of sulfuric and vinyl sulfonic acid etchants on bond strength of resin composite to polyetherketoneketone

Published in: Odontology | Issue 2/2019

Login to get access

Abstract

This study aims to evaluate the effects of etching with sulfuric acid (SA) and vinyl sulfonic acid (VSA) on the bond strength between a light-curing indirect resin composite and polyetherketoneketones (PEKK). PEKK specimens were ground with 600 silicon carbide papers, etched with 90% SA for 5 s (90-5 SA) or 95% VSA for 30 s (95-30 VSA), and then modified with a phosphate primer; afterward, a light-curing resin composite was veneered on the specimens. Two control groups were also prepared without etching (unetched/unprimed and unetched/primed). After 20,000 thermocycles in water at 4 and 60 °C, the shear bond strengths of the specimens were determined and subjected to a nonparametric (Steel–Dwass) test (α = 0.05, n = 8). The etched surfaces were observed by scanning electron microscopy (SEM) at 2000× magnification. Higher bond strengths were obtained when the PEKK surface was etched with 90-5 SA or 95-30 VSA (90-5 SA/unprimed 24.3 ± 4.3 MPa, 90-5 SA/primed 26.2 ± 3.2 MPa, 95-30 VSA/unprimed 23.7 ± 2.5 MPa, 95-30 VSA/primed 24.3 ± 4.1 MPa), and these values were not statistically different, whereas the two control groups exhibited significantly lower bond strengths (unetched/unprimed 12.2 ± 1.7 MPa, unetched/primed 9.5 ± 2.7 MPa). SEM observations revealed that 95-30 VSA led to a microporous (felt-like) surface, which was different from the surface structure etched with 90-5 SA. Etching the PEKK surface with SA or VSA significantly improved the bond strength between resin composite and PEKK in contrast with the application of the phosphate primer. Appropriate chemical etching could be a useful option when fabricating prostheses using PEKK-based materials and indirect resin composites.
Literature
1.
go back to reference Bonner WH. Aromatic polyketones and preparation thereof. United States patent no. 3065205; 1962. Bonner WH. Aromatic polyketones and preparation thereof. United States patent no. 3065205; 1962.
2.
go back to reference Rose JB, Staniland PA. Thermoplastic aromatic polyetherketones. United States patent no. 4320224; 1982. Rose JB, Staniland PA. Thermoplastic aromatic polyetherketones. United States patent no. 4320224; 1982.
3.
go back to reference Fuhrmann G, Steiner M, Freitag-Wolf S, Kern M. Resin bonding to three types of polyaryletherketones (PAEKs)-durability and influence of surface conditioning. Dent Mater. 2014;30:357–63.CrossRef Fuhrmann G, Steiner M, Freitag-Wolf S, Kern M. Resin bonding to three types of polyaryletherketones (PAEKs)-durability and influence of surface conditioning. Dent Mater. 2014;30:357–63.CrossRef
4.
go back to reference Wimmer T, Huffmann AMS, Eichberger M, Schmidlin PR, Stawarczyk B. Two-body wear rate of PEEK, CAD/CAM resin composite and PMMA: effect of specimen geometries, antagonist materials and test set-up configuration. Dent Mater. 2016;32:e127–36.CrossRef Wimmer T, Huffmann AMS, Eichberger M, Schmidlin PR, Stawarczyk B. Two-body wear rate of PEEK, CAD/CAM resin composite and PMMA: effect of specimen geometries, antagonist materials and test set-up configuration. Dent Mater. 2016;32:e127–36.CrossRef
5.
go back to reference Lee WT, Koak JY, Lim YJ, Kim SK, Kwon HB, Kim MJ. Stress shielding and fatigue limits of poly-ether-ether-ketone dental implants. J Biomed Mater Res B Appl Biomater. 2012;100B:1044–52.CrossRef Lee WT, Koak JY, Lim YJ, Kim SK, Kwon HB, Kim MJ. Stress shielding and fatigue limits of poly-ether-ether-ketone dental implants. J Biomed Mater Res B Appl Biomater. 2012;100B:1044–52.CrossRef
6.
go back to reference Schwitalla A, Müller WD. PEEK dental implants: a review of the literature. J Oral Implantol. 2013;39:743–9.CrossRefPubMed Schwitalla A, Müller WD. PEEK dental implants: a review of the literature. J Oral Implantol. 2013;39:743–9.CrossRefPubMed
7.
go back to reference Najeeb S, Zafar MS, Khurshid Z, Siddiqui F. Applications of polyetheretherketone (PEEK) in oral implantology and prosthodontics. J Prosthodont Res. 2016;60:12–9.CrossRef Najeeb S, Zafar MS, Khurshid Z, Siddiqui F. Applications of polyetheretherketone (PEEK) in oral implantology and prosthodontics. J Prosthodont Res. 2016;60:12–9.CrossRef
8.
go back to reference Santing HJ, Meijer HJA, Raghoebar GM, Özcan M. Fracture strength and failure mode of maxillary implant-supported provisional single crowns: a comparison of composite resin crowns fabricated directly over PEEK abutments and solid titanium abutments. Clin Implant Dent Relat Res. 2012;14:882–9.CrossRefPubMed Santing HJ, Meijer HJA, Raghoebar GM, Özcan M. Fracture strength and failure mode of maxillary implant-supported provisional single crowns: a comparison of composite resin crowns fabricated directly over PEEK abutments and solid titanium abutments. Clin Implant Dent Relat Res. 2012;14:882–9.CrossRefPubMed
9.
go back to reference Uhrenbacher J, Schmidlin PR, Keul C, Eichberger M, Roos M, Gernet W, Stawarczyk B. The effect of surface modification on the retention strength of polyetheretherketone crowns adhesively bonded to dentin abutments. J Prosthet Dent. 2014;112:1489–97.CrossRef Uhrenbacher J, Schmidlin PR, Keul C, Eichberger M, Roos M, Gernet W, Stawarczyk B. The effect of surface modification on the retention strength of polyetheretherketone crowns adhesively bonded to dentin abutments. J Prosthet Dent. 2014;112:1489–97.CrossRef
10.
go back to reference Stawarczyk B, Beuer F, Wimmer T, Jahn D, Sener B, Roos M, Schmidlin PR. Polyetheretherketone—a suitable material for fixed dental prostheses? J Biomed Mater Res B Appl Biomater. 2013;101B:1209–16.CrossRef Stawarczyk B, Beuer F, Wimmer T, Jahn D, Sener B, Roos M, Schmidlin PR. Polyetheretherketone—a suitable material for fixed dental prostheses? J Biomed Mater Res B Appl Biomater. 2013;101B:1209–16.CrossRef
11.
go back to reference Stawarczyk B, Thrun H, Eichberger M, Roos M, Edelhoff D, Schweiger J, Schmidlin PR. Effect of different surface pretreatments and adhesives on the load-bearing capacity of veneered 3-unit PEEK FDPs. J Prosthet Dent. 2015;114:666–73.CrossRefPubMed Stawarczyk B, Thrun H, Eichberger M, Roos M, Edelhoff D, Schweiger J, Schmidlin PR. Effect of different surface pretreatments and adhesives on the load-bearing capacity of veneered 3-unit PEEK FDPs. J Prosthet Dent. 2015;114:666–73.CrossRefPubMed
12.
go back to reference Tannous F, Steiner M, Shahin R, Kern M. Retentive forces and fatigue resistance of thermoplastic resin clasps. Dent Mater. 2012;28:273–8.CrossRefPubMed Tannous F, Steiner M, Shahin R, Kern M. Retentive forces and fatigue resistance of thermoplastic resin clasps. Dent Mater. 2012;28:273–8.CrossRefPubMed
13.
go back to reference Kern M, Lehmann F. Influence of surface conditioning on bonding to polyetheretherketon (PEEK). Dent Mater. 2012;28:1280–3.CrossRefPubMed Kern M, Lehmann F. Influence of surface conditioning on bonding to polyetheretherketon (PEEK). Dent Mater. 2012;28:1280–3.CrossRefPubMed
14.
go back to reference Rosentritt M, Preis V, Behr M, Sereno N, Kolbeck C. Shear bond strength between veneering composite and PEEK after different surface modifications. Clin Oral Investig. 2015;19:739–44.CrossRefPubMed Rosentritt M, Preis V, Behr M, Sereno N, Kolbeck C. Shear bond strength between veneering composite and PEEK after different surface modifications. Clin Oral Investig. 2015;19:739–44.CrossRefPubMed
15.
go back to reference Zhou L, Qian Y, Zhu Y, Liu H, Gan K, Guo J. The effect of different surface treatments on the bond strength of PEEK composite materials. Dent Mater. 2014;30:e209-15.CrossRefPubMed Zhou L, Qian Y, Zhu Y, Liu H, Gan K, Guo J. The effect of different surface treatments on the bond strength of PEEK composite materials. Dent Mater. 2014;30:e209-15.CrossRefPubMed
16.
go back to reference Schmidlin PR, Eichberger M, Stawarczyk B. Glycine: a potential coupling agent to bond to helium plasma treated PEEK? Dent Mater. 2016;32:305–10.CrossRefPubMed Schmidlin PR, Eichberger M, Stawarczyk B. Glycine: a potential coupling agent to bond to helium plasma treated PEEK? Dent Mater. 2016;32:305–10.CrossRefPubMed
17.
go back to reference Schmidlin PR, Stawarczyk B, Wieland M, Attin T, Hämmerle CH, Fischer J. Effect of different surface pre-treatments and luting materials on shear bond strength to PEEK. Dent Mater. 2010;26:553–9.CrossRef Schmidlin PR, Stawarczyk B, Wieland M, Attin T, Hämmerle CH, Fischer J. Effect of different surface pre-treatments and luting materials on shear bond strength to PEEK. Dent Mater. 2010;26:553–9.CrossRef
18.
go back to reference Sproesser O, Schmidlin PR, Uhrenbacher J, Roos M, Gernet W, Stawarczyk B. Effect of sulfuric acid etching of polyetheretherketone on the shear bond strength to resin cements. J Adhes Dent. 2014;16:465–72.PubMed Sproesser O, Schmidlin PR, Uhrenbacher J, Roos M, Gernet W, Stawarczyk B. Effect of sulfuric acid etching of polyetheretherketone on the shear bond strength to resin cements. J Adhes Dent. 2014;16:465–72.PubMed
19.
go back to reference Hallmann L, Mehl A, Sereno N, Hämmerle CHF. The improvement of adhesive properties of PEEK through different pre-treatments. Appl Surf Sci. 2012;258:7213–8.CrossRef Hallmann L, Mehl A, Sereno N, Hämmerle CHF. The improvement of adhesive properties of PEEK through different pre-treatments. Appl Surf Sci. 2012;258:7213–8.CrossRef
20.
go back to reference Keul C, Liebermann A, Schmidlin PR, Roos M, Sener B, Stawarczyk B. Influence of PEEK surface modification on surface properties and bond strength to veneering resin composites. J Adhes Dent. 2014;16:383–92.PubMed Keul C, Liebermann A, Schmidlin PR, Roos M, Sener B, Stawarczyk B. Influence of PEEK surface modification on surface properties and bond strength to veneering resin composites. J Adhes Dent. 2014;16:383–92.PubMed
21.
go back to reference Stawarczyk B, Jordan P, Schmidlin PR, Roos M, Eichberger M, Gernet W, Keul C. PEEK surface treatment effects on tensile bond strength to veneering resins. J Prosthet Dent. 2014;112:1278–88.CrossRefPubMed Stawarczyk B, Jordan P, Schmidlin PR, Roos M, Eichberger M, Gernet W, Keul C. PEEK surface treatment effects on tensile bond strength to veneering resins. J Prosthet Dent. 2014;112:1278–88.CrossRefPubMed
22.
go back to reference Stawarczyk B, Silla M, Roos M, Eichberger M, Lümkemann N. Bonding behavior of polyetherketoneketone to methylmethacrylate- and dimethacrylate-based polymers. J Adhes Dent. 2017;19:331–8.PubMed Stawarczyk B, Silla M, Roos M, Eichberger M, Lümkemann N. Bonding behavior of polyetherketoneketone to methylmethacrylate- and dimethacrylate-based polymers. J Adhes Dent. 2017;19:331–8.PubMed
23.
go back to reference Lee KS, Shin MS, Lee JY, Ryu JJ, Shin SW. Shear bond strength of composite resin to high performance polymer PEKK according to surface treatments and bonding materials. J Adv Prosthodont. 2017;9:350–7.CrossRefPubMedPubMedCentral Lee KS, Shin MS, Lee JY, Ryu JJ, Shin SW. Shear bond strength of composite resin to high performance polymer PEKK according to surface treatments and bonding materials. J Adv Prosthodont. 2017;9:350–7.CrossRefPubMedPubMedCentral
24.
go back to reference Tanaka T, Kamada K, Matsumura H, Atsuta M. A comparison of water temperatures for thermocycling of metal-bonded resin specimens. J Prosthet Dent. 1995;74:345–9.CrossRefPubMed Tanaka T, Kamada K, Matsumura H, Atsuta M. A comparison of water temperatures for thermocycling of metal-bonded resin specimens. J Prosthet Dent. 1995;74:345–9.CrossRefPubMed
25.
go back to reference Stawarczyk B, Taufall S, Roos M, Schmidlin PR, Lümkemann N. Bonding of composite resins to PEEK: the influence of adhesive systems and air-abrasion parameters. Clin Oral Investig. 2018;22:763–71.CrossRefPubMed Stawarczyk B, Taufall S, Roos M, Schmidlin PR, Lümkemann N. Bonding of composite resins to PEEK: the influence of adhesive systems and air-abrasion parameters. Clin Oral Investig. 2018;22:763–71.CrossRefPubMed
26.
go back to reference Stawarczyk B, Bähr N, Beuer F, Wimmer T, Eichberger M, Gernet W, Jahn D, Schmidlin PR. Influence of plasma pretreatment on shear bond strength of self-adhesive resin cements to polyetheretherketone. Clin Oral Investig. 2014;18:163–70.CrossRefPubMed Stawarczyk B, Bähr N, Beuer F, Wimmer T, Eichberger M, Gernet W, Jahn D, Schmidlin PR. Influence of plasma pretreatment on shear bond strength of self-adhesive resin cements to polyetheretherketone. Clin Oral Investig. 2014;18:163–70.CrossRefPubMed
27.
go back to reference Stawarczyk B, Keul C, Beuer F, Roos M, Schmidlin PR. Tensile bond strength of veneering resins to PEEK: impact of different adhesives. Dent Mater J. 2013;32:441–8.CrossRefPubMed Stawarczyk B, Keul C, Beuer F, Roos M, Schmidlin PR. Tensile bond strength of veneering resins to PEEK: impact of different adhesives. Dent Mater J. 2013;32:441–8.CrossRefPubMed
28.
go back to reference Xing P, Robertson GP, Guiver MD, Mikhailenko SD, Wang K, Kaliaguine S. Synthesis and characterization of sulfonated poly(ether ether ketone) for proton exchange membranes. J Membr Sci. 2004;229:95–100.CrossRef Xing P, Robertson GP, Guiver MD, Mikhailenko SD, Wang K, Kaliaguine S. Synthesis and characterization of sulfonated poly(ether ether ketone) for proton exchange membranes. J Membr Sci. 2004;229:95–100.CrossRef
29.
go back to reference Shu S, Kobayashi H, Okubo M, Sabarudin A, Butsugan M, Umemura T. Chemical anchoring of lauryl methacrylate-based reversed phase monolith to 1/16″ o.d. polyetheretherketone tubing. J Chromatogr A. 2012;1242:59–66.CrossRefPubMed Shu S, Kobayashi H, Okubo M, Sabarudin A, Butsugan M, Umemura T. Chemical anchoring of lauryl methacrylate-based reversed phase monolith to 1/16″ o.d. polyetheretherketone tubing. J Chromatogr A. 2012;1242:59–66.CrossRefPubMed
30.
go back to reference Zhao Y, Wong HM, Wang W, Li P, Xu Z, Chong EYW, Yan CH, Yeung KWK, Chu PK. Cytocompatibility, osseointegration, and bioactivity of three-dimensional porous and nanostructured network on polyetheretherketone. Biomaterials. 2013;34:9264–77.CrossRefPubMed Zhao Y, Wong HM, Wang W, Li P, Xu Z, Chong EYW, Yan CH, Yeung KWK, Chu PK. Cytocompatibility, osseointegration, and bioactivity of three-dimensional porous and nanostructured network on polyetheretherketone. Biomaterials. 2013;34:9264–77.CrossRefPubMed
31.
go back to reference Taira Y, Matsumura H, Yoshida K, Tanaka T, Atsuta M. Influence of surface oxidation of titanium on adhesion. J Dent. 1998;26:69–73.CrossRefPubMed Taira Y, Matsumura H, Yoshida K, Tanaka T, Atsuta M. Influence of surface oxidation of titanium on adhesion. J Dent. 1998;26:69–73.CrossRefPubMed
Metadata
Title
Effects of sulfuric and vinyl sulfonic acid etchants on bond strength of resin composite to polyetherketoneketone
Publication date
01-04-2019
Published in
Odontology / Issue 2/2019
Print ISSN: 1618-1247
Electronic ISSN: 1618-1255
DOI
https://doi.org/10.1007/s10266-018-0375-0

Other articles of this Issue 2/2019

Odontology 2/2019 Go to the issue