Monolithic and bi-layer CAD/CAM lithium–disilicate versus metal–ceramic fixed dental prostheses: Comparison of fracture loads and failure modes after fatigue

Authors: Stefan Schultheis, Joerg R. Strub, Thomas A. Gerds, Petra C. Guess

Published in: Clinical Oral Investigations | Issue 5/2013

Abstract

Objectives

The authors analyzed the effect of fatigue on the survival rate and fracture load of monolithic and bi-layer CAD/CAM lithium–disilicate posterior three-unit fixed dental prostheses (FDPs) in comparison to the metal–ceramic gold standard.

Materials and methods

The authors divided 96 human premolars and molars into three equal groups. Lithium–disilicate ceramic (IPS-e.max-CAD) was milled with the CEREC-3-system in full-anatomic FDP dimensions (monolithic: M-LiCAD) or as framework (Bi-layer: BL-LiCAD) with subsequent hand-layer veneering. Metal–ceramic FDPs (MC) served as control. Single-load-to-failure tests were performed before and after mouth-motion fatigue.

Results

No fracture failures occurred during fatigue. Median fracture loads in [N], before and after fatigue were, respectively, as follows: M-LiCAD, 1,298/1,900; BL-LiCAD, 817/699; MC, 1,966/1,818. M-LiCAD and MC FPDs revealed comparable fracture loads and were both significantly higher than BL-LiCAD. M-LiCAD and BL-LiCAD both failed from core/veneer bulk fracture within the connector area. MC failures were limited to ceramic veneer fractures exposing the metal core. Fatigue had no significant effect on any group.

Conclusions

Posterior monolithic CAD/CAM fabricated lithium–disilicate FPDs were shown to be fracture resistant with failure load results comparable to the metal–ceramic gold standard. Clinical investigations are needed to confirm these promising laboratory results.

Clinical relevance

Monolithic CAD/CAM fabricated lithium–disilicate FDPs appeared to be a reliable treatment alternative for the posterior load-bearing area, whereas FDPs in bi-layer configuration were susceptible to low load fracture failure.

Pjetursson BE, Lang NP (2008) Prosthetic treatment planning on the basis of scientific evidence. J Oral Rehabil 35:72–79PubMedCrossRef

Donovan TE (2008) Factors essential for successful all-ceramic restorations. J Am Dent Assoc 139(Suppl):14S–18SPubMed

Al-Amleh B, Lyons K, Swain M (2010) Clinical trials in zirconia: a systematic review. J Oral Rehabil 37:641–652PubMed

Coelho PG, Silva NR, Bonfante EA, Guess PC, Rekow ED, Thompson VP (2009) Fatigue testing of two porcelain-zirconia all-ceramic crown systems. Dent Mater 25:1122–1127PubMedCrossRef

Wolfart S, Eschbach S, Scherrer S, Kern M (2009) Clinical outcome of three-unit lithium-disilicate glass-ceramic fixed dental prostheses: up to 8 years results. Dent Mater 25:63–71CrossRef

Guess PC, Zavanelli RA, Silva NR, Bonfante EA, Coehlo P, Thompson VP (2010) Monolithic CAD/CAM lithium disilicate versus veneered Y-TZP crowns: comparison of failure modes and reliability after fatigue. Int J Prosthodont 23:434–442PubMed

Reich S, Fischer S, Sobotta B, Klapper HU, Gozdowski S (2010) A preliminary study on the short-term efficacy of chairside computer-aided design/computer-assisted manufacturing- generated posterior lithium disilicate crowns. Int J Prosthodont 23:214–216PubMed

Fasbinder DJ, Dennison JB, Heys D, Neiva G (2010) A clinical evaluation of chairside lithium disilicate CAD/CAM crowns: a two-year report. J Am Dent Assoc 141(Suppl 2):10S–14SPubMed

Valenti M, Valenti A (2009) Retrospective survival analysis of 261 lithium disilicate crowns in a private general practice. Quint Int 40:573–579

10.

Taskonak B, Sertgoz A (2006) Two-year clinical evaluation of lithia-disilicate-based all-ceramic crowns and fixed partial dentures. Dent Mater 22:1008–1013PubMedCrossRef

11.

Marquardt P, Strub JR (2006) Survival rates of IPS empress 2 all-ceramic crowns and fixed partial dentures: results of a 5-year prospective clinical study. Quint Int 37:253–259

12.

Kern M, Sasse M, Wolfart S (2012) Ten-year outcome of three-unit fixed dental prostheses made from monolithic lithium disilicate ceramic. J Am Dent Assoc 143:234–240PubMed

13.

Krejci I, Reich T, Lutz F, Albertoni M (1990) In-vitro-Testverfahren zur Evaluation dentaler Restaurationssysteme. 1. Computergesteuerter Kausimulator. Schweiz Monatsschr Zahnmed/SSO 100:953–960

14.

DeLong R, Douglas WH (1991) An artificial oral environment for testing dental materials. IEEE transactions on bio-medical engineering 38:339–345PubMedCrossRef

15.

Delong R, Douglas WH (1983) Development of an artificial oral environment for the testing of dental restoratives: bi-axial force and movement control. J Dent Res 62:32–36PubMedCrossRef

16.

Rekow D, Thompson VP (2005) Near-surface damage—a persistent problem in crowns obtained by computer-aided design and manufacturing. Proc Inst Mech Eng [H] 219:233–243CrossRef

17.

Jung YG, Peterson IM, Kim DK, Lawn BR (2000) Lifetime-limiting strength degradation from contact fatigue in dental ceramics. J Dent Res 79:722–731PubMedCrossRef

18.

Heintze SD, Cavalleri A, Zellweger G, Buchler A, Zappini G (2008) Fracture frequency of all-ceramic crowns during dynamic loading in a chewing simulator using different loading and luting protocols. Dent Mater 24:1352–1361PubMedCrossRef

19.

De Boever JA, McCall WD Jr, Holden S, Ash MM Jr (1978) Functional occlusal forces: an investigation by telemetry. J Prosthet Dent 40:326–333PubMedCrossRef

20.

Eichner K (1963) Messung der Kaukräfte bei Kauvorgängen. Dtsch Zahnärztl Z18:915–924

21.

Bates JF, Stafford GD, Harrison A (1976) Masticatory function—a review of the literature. III. Masticatory performance and efficiency. J Oral Rehabil 3:57–67PubMedCrossRef

22.

Kohyama K, Hatakeyama E, Sasaki T, Dan H, Azuma T, Karita K (2004) Effects of sample hardness on human chewing force: a model study using silicone rubber. Arch Oral Biol 49:805–816PubMedCrossRef

23.

Schindler HJ, Stengel E, Spiess WE (1998) Feedback control during mastication of solid food textures—a clinical-experimental study. J Prosthet Dent 80:330–336PubMedCrossRef

24.

Fontijn-Tekamp FA, Slagter AP, Van Der Bilt A, Van THMA, Witter DJ, Kalk W (2000) Biting and chewing in overdentures, full dentures, and natural dentitions. J Dent Res 79:1519–1524PubMedCrossRef

25.

Morneburg TR, Proschel PA (2002) Measurement of masticatory forces and implant loads: a methodologic clinical study. Int J Prosthodont 15:20–27PubMed

26.

Waltimo A, Kononen M (1993) A novel bite force recorder and maximal isometric bite force values for healthy young adults. Scand J Dent Res 101:171–175PubMed

27.

Krejci I, Lutz F (1990) In-vitro-Testverfahren zur Evaluation dentaler Restaurationssysteme. 3. Korrelation mit In-vivo-Resultaten. Schweizer Monatsschri Zahnmed/SSO 100:1445–1449

28.

Chitmongkolsuk S, Heydecke G, Stappert C, Strub JR (2002) Fracture strength of all-ceramic lithium disilicate and porcelain-fused-to-metal bridges for molar replacement after dynamic loading. Eur J Prosthodont Restor Dent 10:15–22PubMed

29.

Att W, Grigoriadou M, Strub JR (2007) ZrO₂ three-unit fixed partial dentures: comparison of failure load before and after exposure to a mastication simulator. J Oral Rehabil 34:282–290PubMedCrossRef

30.

Bahat Z, Mahmood DJ, Vult von Steyern P (2009) Fracture strength of three-unit fixed partial denture cores (Y-TZP) with different connector dimension and design. Swed Dent J33:149–159

31.

Mollers K, Patzold W, Parkot D, Kirsten A, Guth JF, Edelhoff D, Fischer H (2011) Influence of connector design and material composition and veneering on the stress distribution of all-ceramic fixed dental prostheses: a finite element study. Dent Mater 27:e171–e175PubMed

32.

Harder S, Wolfart S, Eschbach S, Kern M (2010) Eight-year outcome of posterior inlay-retained all-ceramic fixed dental prostheses. J Dent 38:875–881PubMedCrossRef

33.

Gonzaga CC, Yoshimura HN, Cesar PF, Miranda WG Jr (2009) Subcritical crack growth in porcelains, glass-ceramics, and glass-infiltrated alumina composite for dental restorations. J Mater Science 20:1017–1024

34.

Wolf D, Bindl A, Schmidlin PR, Luthy H, Mormann WH (2008) Strength of CAD/CAM-generated esthetic ceramic molar implant crowns. Int J Oral & Maxillofac Implant 23:609–617

35.

Sorensen JA, Cruz M, Mito WT, Raffeiner O, Meredith HR, Foser HP (1999) A clinical investigation on three-unit fixed partial dentures fabricated with a lithium disilicate glass-ceramic. Pract Periodontics Aesthet Dent 11:95–106, quiz 8PubMed

36.

Silva NR, Thompson VP, Valverde GB, Coelho PG, Powers JM, Farah JW, Esquivel-Upshaw J (2011) Comparative reliability analyses of zirconium oxide and lithium disilicate restorations in vitro and in vivo. J Am Dent Assoc 142(Suppl 2):4S–9SPubMed

37.

Makarouna M, Ullmann K, Lazarek K, Boening KW (2011) Six-year clinical performance of lithium disilicate fixed partial dentures. Int J Prosthodont 24:204–206PubMed

38.

Gehrt M, Wolfart S, Rafai N, Reich S, Edelhoff D (2012) Clinical results of lithium-disilicate crowns after up to 9 years of service. Clin Oral Invest. doi:10.1007/s00784-012-0700-x

39.

Kim B, Zhang Y, Pines M, Thompson VP (2007) Fracture of porcelain-veneered structures in fatigue. J Dent Res 86:142–146PubMedCrossRef

40.

Castellani D, Baccetti T, Giovannoni A, Bernardini UD (1994) Resistance to fracture of metal ceramic and all-ceramic crowns. Int J Prosthodont 7:149–154PubMed

41.

Anusavice KJ (2012) Standardizing failure, success, and survival decisions in clinical studies of ceramic and metal–ceramic fixed dental prostheses. Dent Mater 28:102–111PubMedCrossRef

42.

Silva NR, Bonfante EA, Zavanelli RA, Thompson VP, Ferencz JL, Coelho PG (2010) Reliability of metalloceramic and zirconia-based ceramic crowns. J Dent Res 89:1051–1056, 26PubMedCrossRef

Title: Monolithic and bi-layer CAD/CAM lithium–disilicate versus metal–ceramic fixed dental prostheses: Comparison of fracture loads and failure modes after fatigue
Authors: Stefan Schultheis
Joerg R. Strub
Thomas A. Gerds
Petra C. Guess
Publication date: 01-06-2013
Publisher: Springer-Verlag
Published in: Clinical Oral Investigations / Issue 5/2013
Print ISSN: 1432-6981
Electronic ISSN: 1436-3771
DOI: https://doi.org/10.1007/s00784-012-0830-1

ACC 2024 Congress

Springer Medicine

Monolithic and bi-layer CAD/CAM lithium–disilicate versus metal–ceramic fixed dental prostheses: Comparison of fracture loads and failure modes after fatigue

Abstract

Objectives

Materials and methods

Results

Conclusions

Clinical relevance

ACC 2024 Congress

Springer Medicine

Abstract

Objectives

Materials and methods

Results

Conclusions

Clinical relevance

Please log in to get access to this content

Other articles of this Issue 5/2013

Proliferation and osteogenic differentiation of osteoblast-like cells obtained from two techniques for harvesting intraoral bone grafts

Randomized controlled clinical trial on the three-dimensional accuracy of fast-set impression materials

Complications and survival rates of teeth after dental trauma over a 5-year period

Effect of polymerisation and ageing on the incremental bond strength of ormocer-based dental materials

Is there a relationship between hyperactivity/inattention symptoms and poor oral health? Results from the GINIplus and LISAplus study

Three-dimensional analysis of tooth dimensions in the MSX1-missense mutation