01-05-2014 | Original Article

Push-out bond strength of three calcium silicate cements to root canal dentine after two different irrigation regimes

Authors: Davut Çelik, Kürşat Er, Ahmet Serper, Tamer Taşdemir, Kadir Tolga Ceyhanlı

Published in: Clinical Oral Investigations | Issue 4/2014

Abstract

Objectives

The aim of this study was to compare the push-out bond strength of three calcium silicate cements to dentine after two different irrigation regimes.

Materials and methods

One hundred eighty 2-mm-thick root sections were prepared. The sections were divided into three main groups (n = 60). In group A, the sections were immersed in 1 % NaOCl for 3 min. In group B, the sections were immersed in 17 % EDTA for 3 min followed by 1 % NaOCl for the same period of time. In group C (control group), no irrigation was applied to the sections. The samples from each group were divided into four subgroups (n = 15). In subgroups A1, B1 and C1, DiaRoot BioAggregate; in subgroups A2, B2 and C2, MTA-Angelus and in subgroups A3, B3 and C3, MM-MTA were mixed with hand-mixing. In subgroups A4, B4 and C4, MM-MTA was mixed with auto-mixing. The mixed cements were then placed into cavities with a carrier. The samples were submitted to the push-out test and were loaded. All the data were analysed with one-way analysis of variance and the Tukey HSD multiple comparisons (p < 0.05).

Results

There were no statistically significant differences between the irrigation regimes regardless of the used materials. The resistance to displacement in subgroup B4 was significantly greater than that presented by subgroups A3, B3 and C3 (p < 0.05) while not different than all other groups.

Conclusions

Irrigation regimes had not affected the push-out bond strength of the calcium silicate cements. Also, strength of auto-mixed MM-MTA was similar to the other cements.

Clinical relevance

The novel calcium silicate cements would be a potentially useful material in endodontic procedures with favourable properties.

Gancedo-Caravia L, Garcia-Barbero E (2006) Influence of humidity and setting time on the push-out strength of mineral trioxide aggregate obturations. J Endod 32:894–6PubMedCrossRef

Parirokh M, Torabinejad M (2010) Mineral trioxide aggregate: a comprehensive literature review-Part I: chemical, physical, and antibacterial properties. J Endod 36:16–27PubMedCrossRef

Shokouhinejad N, Nekoofar MH, Iravani A, Kharrazifard MJ, Dummer PM (2010) Effect of acidic environment on the push-out bond strength of mineral trioxide aggregate. J Endod 36:871–4PubMedCrossRef

Hong ST, Bae KS, Baek SH, Kum KY, Shon WJ, Lee W (2010) Effects of root canal irrigants on the push-out strength and hydration behaviour of accelerated mineral trioxide aggregate in its early setting phase. J Endod 36:1995–9PubMedCrossRef

Saghiri MA, Shokouhinejad N, Lotfi M, Aminsobhani M, Saghiri AM (2010) Push-out bond strength of mineral trioxide aggregate in the presence of alkaline pH. J Endod 36:1856–9PubMedCrossRef

Shahi S, Rahimi S, Yavari HR, Samiei M, Janani M, Bahari M, Abdolrahimi M, Pakdel F, Aghbali A (2012) Effects of various mixing techniques on push-out bond strengths of white mineral trioxide aggregate. J Endod 38:501–4PubMedCrossRef

Drummond JL, Sakaquchi RL, Racean DC, Wozny J, Steinberg AD (1996) Testing mode and surface treatment effects on dentin bonding. J Biomed Mat Res 32:533–41CrossRef

Apaydin ES, Shabahang S, Torabinejad M (2004) Hard-tissue healing after application of fresh or set MTA as root-end-filling material. J Endod 30:21–4PubMedCrossRef

Hakki SS, Bozkurt SB, Ozcopur B, Purali N, Belli S (2012) Periodontal ligament fibroblast response to root perforations restored with different materials—a laboratory study. Int Endod J 45:240–8PubMedCrossRef

10.

Hakki SS, Bozkurt SB, Hakki EE, Belli S (2009) Effects of mineral trioxide aggregate on cell survival gene expression associated with mineralized tissues and biomineralization of cementoblasts. J Endod 35:513–9PubMedCrossRef

11.

Karabucak B, Li D, Lim J, Iqbal M (2005) Vital pulp therapy with mineral trioxide aggregate. Dent Traumatol 21:240–3PubMedCrossRef

12.

Felippe WT, Felippe MCS, Rocha MJC (2006) The effect of mineral trioxide aggregate on the apexification and periapical healing of teeth with incomplete root formation. Int Endod J 39:2–9PubMedCrossRef

13.

Cehreli ZC, Isbitiren B, Sara S, Erbas G (2011) Regenerative endodontic treatment (revascularization) of immature necrotic molars medicated with calcium hydroxide: a case series. J Endod 37:1327–30PubMedCrossRef

14.

Bogen G, Kuttler S (2009) Mineral trioxide aggregate obturation: a review and case series. J Endod 35:777–90PubMedCrossRef

15.

Parirokh M, Torabinejad M (2010) Mineral trioxide aggregate: a comprehensive literature review—Part III: clinical pplications, drawbacks, and mechanism of action. J Endod 36:400–13PubMedCrossRef

16.

De-Deus G, Canabarro A, Alves G, Linhares A, Senne MI, Granjeiro JM (2009) Optimal cytocompatibility of a bioceramic nanoparticulate cement in primary human mesenchymal cells. J Endod 35:1387–90PubMedCrossRef

17.

Zhang H, Pappen G, Haapasalo M (2009) Dentin enhances the antibacterial effect of mineral trioxide aggregate and bioaggregate. J Endod 35:221–4PubMedCrossRef

18.

Reyes-Carmona JF, Felippe MS, Felippe WT (2010) The biomineralization ability of mineral trioxide aggregate and portland cement on dentin enhances the push-out strength. J Endod 36:286–91PubMedCrossRef

19.

Torabinejad M, Parirokh M (2010) Mineral trioxide aggregate: a comprehensive literature review—part II: leakage and biocompatibility investigations. J Endod 36:190–202PubMedCrossRef

20.

Kayahan MB, Nekoofar MH, Kazandağ M, Canpolat C, Malkondu O, Kaptan F, Dummer PM (2009) Effect of acid-etching procedure on selected physical properties of mineral trioxide aggregate. Int Endod J 42:1004–14PubMedCrossRef

21.

VanderWeele RA, Schwartz SA, Beeson TJ (2006) Effect of blood contamination on retention characteristics of MTA when mixed with different liquids. J Endod 32:421–4PubMedCrossRef

22.

Hashem AAR, Wanees Amin SA (2009) The effect of acidity on dislodgment resistance of mineral trioxide aggregate and bioaggregate in furcation perforations: an in vitro comparative study. J Endod 38:245–9CrossRef

23.

El-Ma'aita AM, Qualtrough AJE, Watts DC (2012) A Micro-computed tomography evaluation of mineral trioxide aggregate root canal fillings. J Endod 38:670–2PubMedCrossRef

24.

Aminoshariae A, Hartwell GR, Moon PC (2003) Placement of mineral trioxide aggregate using two different techniques. J Endod 29:679–82PubMedCrossRef

25.

Yeung P, Liewehr FR, Moon PC (2006) A quantitative comparison of the fill density of MTA produced by two placement techniques. J Endod 32:456–9PubMedCrossRef

26.

Namazikhah MS, Nekoofar MH, Sheykhrezae MS, Salariyeh S, Hayes SJ, Bryant ST, Mohammadi MM, Dummer PM (2008) The effect of pH on surface hardness and microstructure of mineral trioxide aggregate. Int Endod J 41:108–16PubMed

27.

Nekoofar MH, Haddad DC, Nodle J, Aseeley Z (2009) Water content of ampoule packaged with ProRoot MTA. Int Endod J 42:205–10

28.

Nekoofar MH, Aseeley Z, Dummer PM (2010) The effect of various mixing techniques on the surface microhardness of mineral trioxide aggregate. Int Endod J 43:312–20PubMedCrossRef

29.

Timpawat S, Vongsavan N, Messer HH (2001) Effect of removal of the smear layer on apical microleakage. J Endod 27:351–3PubMedCrossRef

30.

Meryon SD, Brook AM (1990) Penetration of dentine by three oral bacteria in vitro and their associated cytotoxicity. Int Endod J 23:196–202PubMedCrossRef

31.

Oksan T, Aktener BO, Sen BH, Tezel H (1993) The penetration of root canal sealers into dentinal tubules: a scanning electron microscope study. Int Endod J 26:301–5PubMedCrossRef

32.

Yan P, Peng B, Fan B, Fan M, Bian Z (2006) The effects of sodium hypochlorite (5.25%), chlorhexidine (2%), and glyde file prep on the bond strength of MTA-dentin. J Endod 32:58–60PubMedCrossRef

33.

Lee YL, Lin FH, Wang WH, Ritchie HH, Lan WH, Lin CP (2007) Effects of EDTA on the hydration mechanism of mineral trioxide aggregate. J Dent Res 86:534–8PubMedCrossRef

34.

Smith JB, Loushine RJ, Weller RN, Rueggeberg FA, Whitford GM, Pashley DH, Tay FR (2007) Metrologic evaluation of the surface of white MTA after the use of two endodontic irrigants. J Endod 33:463–7PubMedCrossRef

35.

Uyanik MO, Nagas E, Sahin C, Dagli F, Cehreli ZC (2009) Effects of different irrigation regimens on the sealing properties of repaired furcal perforations. Oral Surg Oral Med Oral Pathol Oral Radiol Endod 107:e91–5PubMedCrossRef

36.

Yildirim T, Oruçoğlu H, Cobankara FK (2008) Long-term evaluation of the influence of smear layer on the apical sealing ability of MTA. J Endod 34:1537–40PubMedCrossRef

Title: Push-out bond strength of three calcium silicate cements to root canal dentine after two different irrigation regimes
Authors: Davut Çelik
Kürşat Er
Ahmet Serper
Tamer Taşdemir
Kadir Tolga Ceyhanlı
Publication date: 01-05-2014
Publisher: Springer Berlin Heidelberg
Published in: Clinical Oral Investigations / Issue 4/2014
Print ISSN: 1432-6981
Electronic ISSN: 1436-3771
DOI: https://doi.org/10.1007/s00784-013-1082-4

Keynote webinar | Spotlight on medication adherence

Springer Medicine

Push-out bond strength of three calcium silicate cements to root canal dentine after two different irrigation regimes

Abstract

Objectives

Materials and methods

Results

Conclusions

Clinical relevance

Keynote webinar | Spotlight on medication adherence

Springer Medicine

Abstract

Objectives

Materials and methods

Results

Conclusions

Clinical relevance

Please log in to get access to this content

Other articles of this Issue 4/2014

Fluoride release and mechanical properties after 1-year water storage of recent restorative glass ionomer cements

Cheek rotation flap reconstruction—an anthropometric appraisal of surgical outcomes

Incidental findings on cone beam computed tomography scans in cleft lip and palate patients

A novel three-dimensional analysis of standardized bone defects by means of confocal scanner and micro-computed tomography

In vitro culture system for keratinocytes obtained from oral lichen planus lesions

Effect of pulverized natural bone mineral on regeneration of three-wall intrabony defects. A preclinical study