Novel magnetic nanocomposite injectables: calcium phosphate cements impregnated with ultrafine magnetic nanoparticles for bone regeneration
Abstract
Self-setting calcium phosphate cements (CPCs) are some of the few injectables of bioceramic materials applicable to bone repair. Incorporation of nanoparticulates to CPCs is considered a promising process that can improve the mechanical and biological properties of CPCs. Here, we added magnetic nanoparticles (MNPs) at small contents, and examined their effects on the physico-chemical, mechanical, and in vitro biological properties of the CPC composition. The MNPs were coated with a silica layer and had an average size of ∼80 nm. The addition of MNPs did not alter the setting reaction, but dramatically changed the crystal shape and size of the transformed hydroxyapatite, from large plate-like crystals to small needle-like crystals. Mechanical strength was significantly improved from 22 MPa to 33 MPa with the addition of only 0.1% MNPs. A striking difference in cell adhesion of rat bone marrow stromal cells was noticed with the MNPs-incorporation. The cells adhered and spread more actively to the MNP-added CPCs than to the pure CPCs with an approximately 2.5-fold and 4.5-fold increase in cell adhesion and in cell spreading area, respectively. The cell proliferative potential lasted for a longer period of up to 14 days where osteogenic differentiation, determined by alkaline phosphatase activity, was also substantially stimulated by the MNP-incorporation. The results indicate that only a small incorporation of ultrafine MNPs changed the properties of CPCs dramatically, making them more suitable for use in cell culture and repair of bone tissues.
Please wait while we load your content...